10CrMo910asye anjeneral gen apeprè {{0}}.08-0.15% kabòn, 0.40-0.70% Silisyòm, 0 .50-1.00% Manganèz, 0.{{10}}.65% Kwòm, 0.04% Fosfò, 0.012% Souf, 0.{{17} }.60% molybdène, ak ti kantite lòt eleman alyaj.
DIN 17175 10CrMo910 tiyo yo oblije satisfè pwopriyete mekanik espesifik, ki gen ladan fòs rupture minimòm, fòs sede, ak elongasyon. Pwopriyete sa yo asire kapasite tiyo yo pou kenbe tèt ak kondisyon wo-tanperati ak presyon-wo.
Tanperati tretman chalè DIN 17175 10CrMo910 Tib asye san pwoblèm
| Steel Klas | Degre pwosesis tèmik | Nòmalize degre | Tanperaman | ||
| Klas | Nimewo materyèl | Trempe degre tanperati | Tanperati degre | ||
| 10CrMo910 | 1.7380 | 1100 a 850 degre | - | 900-960 | 700-750 |
Konpozisyon chimik DIN 17175 10CrMo910
| Estanda: DIN 17175 | klas | Konpozisyon chimik | |||||
| C | Si | Mn | P,S | Kr | Mo | ||
| 10CrMo910 | 0.08-0.15 | Mwens pase oswa egal a 0.50 | 0.40-0.70 | Mwens pase oswa egal a 0.030 | 2.00-2.50 | 0.90-1.20 | |
Pwopriyete mekanik DIN 17175 10CrMo910
| Estanda | klas | Fòs rupture (MPa) | Sede fòs (MPa) | elongasyon (%) |
| DIN 17175 | 10CrMo910 | 450-600 | Pi gran pase oswa egal a 280 | Pi gran pase oswa egal a 18 |
Dimansyon tolerans
| Pwojè | Estanda | Ranje gwosè | Tolerans | |||
| Dyamèt ekstèn | DIN17175 | Cho woule tiyo asye | OD mwens pase oswa egal a 100mm | ± {{0}}.75% (Min ± 0.5mm) | ||
| OD＞ 100 ~ 320mm | ± 0.9% | |||||
| Fwad trase tiyo asye OD Mwens pase oswa egal a 120mm | ± {{0}}.6% (Min ± 0.25mm) | |||||
| Epesè miray la | DIN17175 | OD mwens pase oswa egal a 130mm | WT Mwens pase oswa egal a 2Sn | +15%~-10% | ||
| WT ＞ 2Sn ~ 4Sn | +12.5%~-10% | |||||
| WT ＞ 4Sn | ± 9% | |||||
| 130 ＜ OD Mwens pase oswa egal a 320mm | WT Mwens pase oswa egal a 0.05OD | +17.5%~-12.5% | ||||
| {{0}}.05OD ＜ WT Mwens pase oswa egal a 0.11OD | ± 12.5% | |||||
| WT ＞ 0.11OD | ± 10% | |||||
Konpayi an gen yon avantaj konpetitif enpòtan nan mache a, ki soti nan bon jan kalite pwodwi nou yo, teknoloji manifakti avanse, sèvis kliyan ekselan ak pri konpetitif. Eksperyans solid nou yo ak ekselan sistèm asirans kalite te fè nou premye chwa nan kliyan nou yo, fè nou jwenn konfyans toupatou pa sèlman nan mache domestik la, men tou nan mache entènasyonal la.