Nov 05, 2025
Tiyo alyaj presyon se yon kalite tiyo san pwoblèm presyon-pote prensipalman yo itilize pou transmèt likid, gaz, oswa kòm konpozan presyon nan gwo-tanperati ak segondè-ekipman presyon. Yo souvan jwenn nan aplikasyon tankou chodyèr, plant pétrochimique, ak perçage jewolojik. Manifaktire nan estanda ki gen ladan A213, A335, ak A209, materyèl tipik yo enkli T9/P9, T1, T11, P11, T91, P91, elatriye. Tiyo sa yo dwe satisfè espesifikasyon teknik tankou fòs ranpe ak rezistans oksidasyon.
Spesifikasyon
|
Pwodwi |
Segondè Tanperati Alloy Steel Tib, Tiyo Presyon Alloy |
|
Aplikasyon |
Nan petwòl, Aerospace, chimik, pouvwa, chodyèr, endistri militè |
|
Estanda tiyo |
ASTM A335/A213/A209/ASME SA335/SA213/SA209/DIN17175/JIS G3462 |
|
Gwosè |
OD: 1/8'' - 26'' |
|
WT: SCH 10, 30, 40, 60, 80, 120, 140, 160, XS, XXS, STD |
|
|
Longè: Single Random, Double Random, Koupe Longè |
|
| Materyèl tib | Alyaj asye ak asye pur |
| Klas | T9, T11, T12, T21, T22, T91 ak klas pur nan TP304 oswa TP316 |
|
NPS, pous |
Dyamèt deyò (mm) |
Epesè miray (mm) |
Max. Longè (M) |
|
1/8 |
10,3 |
1,24; 1,73; 2,40 |
12 |
|
1/4 |
13,7 |
1,65; 2,24; 3,02 |
|
|
3/8 |
17,1 |
1,65; 2,31; 3,20 |
|
|
1/2 |
21,3 |
1,65; 2,11; 2,77; 3,73 |
|
|
3/4 |
26,7 |
1,65; 2,11; 2,87; 3,91 |
|
|
1 |
33,4 |
1,65; 2,77; 3,38; 4,55 |
10 |
|
1 1/4 |
42,4 |
1,65; 2,77; 3,56; 4,85 |
|
|
1 1/2 |
48,3 |
2,77; 3,68; 5,08 |
|
|
2 |
60,3 |
3,91; 5,54 |
7 |
ASTM A213 Alloy Steel Chimik Konpozisyon (%, max)
|
Steel Klas |
Konpozisyon chimik% |
||||||||||||
|
C |
Si |
Mn |
P, S Max |
Kr |
Mo |
Ni Max |
V |
Al Max |
W |
B |
Nb |
N |
|
|
T2 |
0.10~0.20 |
0.10~0.30 |
0.30~0.61 |
0.025 |
0.50~0.81 |
0.44~0.65 |
– |
– |
– |
– |
– |
– |
– |
|
T11 |
0.05~0.15 |
0.50~1.00 |
0.30~0.60 |
0.025 |
1.00~1.50 |
0.44~0.65 |
– |
– |
– |
– |
– |
– |
– |
|
T12 |
0.05~0.15 |
Maksimòm 0.5 |
0.30~0.61 |
0.025 |
0.80~1.25 |
0.44~0.65 |
– |
– |
– |
– |
– |
– |
– |
|
T22 |
0.05~0.15 |
Maksimòm 0.5 |
0.30~0.60 |
0.025 |
1.90~2.60 |
0.87~1.13 |
– |
– |
– |
– |
– |
– |
– |
|
T91 |
0.07~0.14 |
0.20~0.50 |
0.30~0.60 |
0.02 |
8.0~9.5 |
0.85~1.05 |
0.4 |
0.18~0.25 |
0.015 |
– |
– |
0.06~0.10 |
0.03~0.07 |
|
T92 |
0.07~0.13 |
Maksimòm 0.5 |
0.30~0.60 |
0.02 |
8.5~9.5 |
0.30~0.60 |
0.4 |
0.15~0.25 |
0.015 |
1.50~2.00 |
0.001~0.006 |
||
ASTM A213 Alloy Steel pwopriyete mekanik:
|
Steel Klas |
Pwopriyete mekanik |
|||
|
T. S |
Y. P |
Elongasyon |
Dite |
|
|
T2 |
Pi gran pase oswa egal a 415MPa |
Pi gran pase oswa egal a 205MPa |
Pi gran pase oswa egal a 30% |
163HBW(85HRB) |
|
T11 |
Pi gran pase oswa egal a 415MPa |
Pi gran pase oswa egal a 205MPa |
Pi gran pase oswa egal a 30% |
163HBW(85HRB) |
|
T12 |
Pi gran pase oswa egal a 415MPa |
Pi gran pase oswa egal a 220MPa |
Pi gran pase oswa egal a 30% |
163HBW(85HRB) |
|
T22 |
Pi gran pase oswa egal a 415MPa |
Pi gran pase oswa egal a 205MPa |
Pi gran pase oswa egal a 30% |
163HBW(85HRB) |
|
T91 |
Pi gran pase oswa egal a 585MPa |
Pi gran pase oswa egal a 415MPa |
Pi gran pase oswa egal a 20% |
250HBW (25HRB) |
|
T92 |
Pi gran pase oswa egal a 620MPa |
Pi gran pase oswa egal a 440MPa |
Pi gran pase oswa egal a 20% |
250HBW (25HRB) |
ASTM A213 Steel Tib Deyò Dyamèt ak Mi Pesè Tolerans
|
OD, mm |
OD Tolerans |
|
< 25.4 |
+/- 0.10 |
|
25.4 – <= 38.1 |
+/- 0.15 |
|
> 38.1 -< 50.8 |
+/- 0.20 |
|
50.8 -< 63.5 |
+/- 0.25 |
|
63.5 -< 76.2 |
+/- 0.30 |
|
76.2 – <= 101.6 |
+/- 0.38 |
|
> 101.6 – <= 190.5 |
+0.38/-0.64 |
|
> 190.5 – <= 228.6 |
+0.38/-1.14 |
|
OD, mm |
WT tolerans |
|
<= 38.1 |
+20%/-0 |
|
> 38.1 |
+22%/-0 |
ASTM A209 Alloy Steel Chimik Konpozisyon
|
Konpozan chimik (%) |
||||||
|
Klas |
C |
Mn |
P |
S |
Si |
Mo |
|
T1 |
0.10-0.20 |
0.30-0.80 |
Mwens pase oswa egal a 0.025 |
Mwens pase oswa egal a 0.025 |
0.10-0.50 |
0.44-0.65 |
|
T1a |
0.15-0.25 |
0.30-0.80 |
Mwens pase oswa egal a 0.025 |
Mwens pase oswa egal a 0.025 |
0.10-0.50 |
0.44-0.65 |
|
T1b |
0.14 max |
0.30-0.80 |
Mwens pase oswa egal a 0.025 |
Mwens pase oswa egal a 0.025 |
0.10-0.50 |
0.44-0.65 |
ASTM A209 Alloy Steel Pwopriyete mekanik:
|
Klas |
Tensile |
Sede |
Elongasyon |
Dite |
|
Fòs (Mpa) |
Fòs (Mpa) |
(%) |
(HRB) |
|
|
T1 |
Pi gran pase oswa egal a 380 |
Pi gran pase oswa egal a 205 |
Pi gran pase oswa egal a 30 |
Mwens pase oswa egal a 80 |
|
T1a |
Pi gran pase oswa egal a 365 |
Pi gran pase oswa egal a 195 |
Pi gran pase oswa egal a 30 |
Mwens pase oswa egal a 81 |
|
T1b |
Pi gran pase oswa egal a 415 |
Pi gran pase oswa egal a 220 |
Pi gran pase oswa egal a 30 |
Mwens pase oswa egal a 77 |
Dyamèt deyò ak tolerans:
|
Woule cho |
Dyamèt deyò, mm |
Tolerans, mm |
|
OD Mwens pase oswa egal a 101.6 |
+0.4/-0.8 |
|
|
101.6＜OD Mwens pase oswa egal a 190.5 |
+0.4/-1.2 |
|
|
190.5＜OD Mwens pase oswa egal a 228.6 |
+0.4/-1.6 |
|
|
Fwad trase |
Dyamèt deyò, mm |
Tolerans, mm |
|
OD＜25.4 |
±0.10 |
|
|
25.4 Mwens pase oswa egal a OD Mwens oswa egal a 38.1 |
±0.15 |
|
|
38.1＜OD＜50.8 |
±0.20 |
|
|
50.8 Mwens pase oswa egal a OD＜63.5 |
±0.25 |
|
|
63.5 Mwens pase oswa egal a OD＜76.2 |
±0.30 |
|
|
76.2 Mwens oswa egal a OD Mwens oswa egal a 101.6 |
±0.38 |
|
|
101.6＜OD Mwens pase oswa egal a 190.5 |
+0.38/-0.64 |
|
|
190.5＜OD Mwens pase oswa egal a 228.6 |
+0.38/-1.14 |
Epesè miray ak tolerans:
|
Woule cho |
Dyamèt deyò, mm |
Tolerans, % |
|
OD mwens pase oswa egal a 101.6, WT mwens pase oswa egal a 2.4 |
+40/-0 |
|
|
OD mwens pase oswa egal a 101.6, 2.4＜WT mwens pase oswa egal a 3.8 |
+35/-0 |
|
|
OD mwens pase oswa egal a 101.6, 3.8＜WT mwens pase oswa egal a 4.6 |
+33/-0 |
|
|
OD≤101.6, WT>4.6 |
+28/-0 |
|
|
OD>101.6, 2.4＜WT Mwens pase oswa egal a 3.8 |
+35/-0 |
|
|
OD>101.6, 3.8＜WT Mwens oswa egal a 4.6 |
+33/-0 |
|
|
OD>101.6, WT>4.6 |
+28/-0 |
|
|
Fwad trase |
Dyamèt deyò, mm |
Tolerans, % |
|
OD Mwens pase oswa egal a 38.1 |
+20/-0 |
|
|
OD>38.1 |
+22/-0 |
Kondisyon chimik nan A335 Alloy Steel tiyo san pwoblèm
|
Klas |
UNS |
C Mwens pase oswa egal a |
Mn |
P Mwens pase oswa egal a |
S Mwens pase oswa egal a |
Si mwens pase oswa egal a |
Kr |
Mo |
|
P1 |
K11522 |
0.10~0.20 |
0.30~0.80 |
0.025 |
0.025 |
0.10~0.50 |
- |
0.44~0.65 |
|
P2 |
K11547 |
0.10~0.20 |
0.30~0.61 |
0.025 |
0.025 |
0.10~0.30 |
0.50~0.81 |
0.44~0.65 |
|
P5 |
K41545 |
0.15 |
0.30~0.60 |
0.025 |
0.025 |
0.50 |
4.00~6.00 |
0.44~0.65 |
|
P5b |
K51545 |
0.15 |
0.30~0.60 |
0.025 |
0.025 |
1.00~2.00 |
4.00~6.00 |
0.44~0.65 |
|
P5c |
K41245 |
0.12 |
0.30~0.60 |
0.025 |
0.025 |
0.50 |
4.00~6.00 |
0.44~0.65 |
|
P9 |
S50400 |
0.15 |
0.30~0.60 |
0.025 |
0.025 |
0.50~1.00 |
8.00~10.00 |
0.44~0.65 |
|
P11 |
K11597 |
0.05~0.15 |
0.30~0.61 |
0.025 |
0.025 |
0.50~1.00 |
1.00~1.50 |
0.44~0.65 |
|
P12 |
K11562 |
0.05~0.15 |
0.30~0.60 |
0.025 |
0.025 |
0.50 |
0.80~1.25 |
0.44~0.65 |
|
P15 |
K11578 |
0.05~0.15 |
0.30~0.60 |
0.025 |
0.025 |
1.15~1.65 |
- |
0.44~0.65 |
|
P21 |
K31545 |
0.05~0.15 |
0.30~0.60 |
0.025 |
0.025 |
0.50 |
2.65~3.35 |
0.80~1.60 |
|
P22 |
K21590 |
0.05~0.15 |
0.30~0.60 |
0.025 |
0.025 |
0.50 |
1.90~2.60 |
0.87~1.13 |
|
P91 |
K91560 |
0.08~0.12 |
0.30~0.60 |
0.020 |
0.010 |
0.20~0.50 |
8.00~9.50 |
0.85~1.05 |
|
P92 |
K92460 |
0.07~0.13 |
0.30~0.60 |
0.020 |
0.010 |
0.50 |
8.50~9.50 |
0.30~0.60 |
Kondisyon pou Tensile nan A335 Alloy Steel tiyo san pwoblèm
|
San pwoblèm |
|||||
|
P-5 |
P-9 |
P-11 |
P-22 |
P-91 |
|
|
Fòs rupture, min., psi |
|||||
|
ksi |
60 |
60 |
60 |
60 |
85 |
|
MPa |
415 |
415 |
415 |
415 |
585 |
|
Fòs Sede, min., psi |
|||||
|
ksi |
30 |
30 |
30 |
30 |
60 |
|
MPa |
205 |
205 |
205 |
205 |
415 |
Tolerans pou ASTM A335/ASME SA 335 P5, P9, P11, P22, P91 tiyo san pwoblèm
|
NPS |
OD Tolerans |
NPS |
WT tolerans |
|
1/8" Mwens pase oswa egal a NPS Mwens pase oswa egal a 1 1/2" |
+/- 0.4 |
1/8" Mwens pase oswa egal a NPS Mwens pase oswa egal a 2 1/2" , Tout rapò T/D. |
+20%, -12.5% |
|
1 1/2 < NPS Mwens pase oswa egal a 4" |
+/- 0.79 |
NPS Pi gran pase oswa egal a 2 1/2" , T/D Mwens pase oswa egal a 5% |
+22.5%, -12.5% |
|
4" < NPS Mwens pase oswa egal a 8" |
+1.59, -0.79 |
NPS Pi gran pase oswa egal a 2 1/2" , T/D > 5% |
+15%, -12.5% |
|
8" < NPS Mwens pase oswa egal a 12" |
+2.38, -0.79 |
(T= Espesifye Mi Epesè; D=Espesifye Dyamèt Deyò) |
|
|
NPS > 12" |
+/- 1% |
||
Pwosesis
Anbalaj
Pake pake
Pake bwat an bwa