Tib chodyè san pwoblèm 15Mo3

DIN 17175 15Mo3 Alloy Steel Tiyo Spesifikasyon Orè

Estanda:DIN 17175

Gamme Pwovizyon pou GNEE: DIN 17175 tib chodyè san pwoblèm,DIN17175 ST35.8 Tib chodyè, DIN17175 ST45.8 Tib chodyè, DIN17175 15Mo3 tib san pwoblèm, DIN17175 13CrMo44 tib san pwoblèm, DIN17175 10CrMo910 tib san pwoblèm, DIN17175 tib san pwoblèm.

Gwosè:19mm-350mm

W.T.:1.5mm-50mm

Fòm:Round

Kalite pwodiksyon:Fwad trase oswa cho woule

Longè:Single longè o aza / Double longè o aza oswa kòm demann aktyèl kliyan an maksimòm longè se 10m

Klas:ST35.8, ST45.8, 15Mo3, 13CrMo44, 10CrMo91

Tanperati tretman chalè DIN 17175 15Mo3 Tib asye san pwoblèm

Steel Klas		Degre pwosesis tèmik	Nòmalize degre	Tanperaman
Klas	Nimewo materyèl			Trempe degre tanperati	Tanperati degre
15mo3	1.5415	1100 a 850 degre	910-940	-	-

Konpozisyon chimik DIN 17175 15Mo3 Alloy Steel Tiyo

Estanda: DIN 17175	klas	Konpozisyon chimik
		C	Si	Mn	P,S	Kr	Mo
	15mo3	0.12-0.20	0.10-0.35	0.40-0.80	Mwens pase oswa egal a 0.030	/	0.25-0.35

Pwopriyete mekanik DIN 17175 15Mo3 Tib chodyè san pwoblèm

Estanda	klas	Fòs rupture (MPa)	Sede fòs (MPa)	elongasyon (%)
DIN 17175	15mo3	450-600	Pi gran pase oswa egal a 270	Pi gran pase oswa egal a 20

Dimansyon Tolerans nan DIN17175 15Mo3 Tib asye san pwoblèm pou Tanperati Elve

Pwojè	Estanda		Ranje gwosè		Tolerans
Dyamèt ekstèn	DIN17175		Cho woule tiyo asye	OD mwens pase oswa egal a 100mm	± {{0}}.75% (Min ± 0.5mm)
				OD＞ 100 ~ 320mm	± 0.9%
			Fwad trase tiyo asye OD Mwens pase oswa egal a 120mm		± {{0}}.6% (Min ± 0.25mm)
Epesè miray la	DIN17175	OD mwens pase oswa egal a 130mm	WT Mwens pase oswa egal a 2Sn		+15%~-10%
			WT ＞ 2Sn ~ 4Sn		+12.5%~-10%
			WT ＞ 4Sn		± 9%
		130 ＜ OD Mwens pase oswa egal a 320mm	WT Mwens pase oswa egal a 0.05OD		+17.5%~-12.5%
			{{0}}.05OD ＜ WT Mwens pase oswa egal a 0.11OD		± 12.5%
			WT ＞ 0.11OD		± 10%

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Gwoup GNEE espesyalize nan founi tiyo alyaj frèt trase, tiyo chodyè frèt, tiyo chodyè woule cho, tiyo alyaj cho woule, elatriye.konsiltenenpòt ki lè.